Dangi taurin Materials da ma'adanai

relative_hardness_of_materials_and_minerals500
  •  

  •  1. Diamond
  •  2. Boron carbide
  •  3. Vanadium carbide
  •  4. Silicon carbide
  •  5. Titanium carbide
  •  6. Corundum
  •  7. Tungsten carbide
  •  8. Molybdenum carbide
  •  9. Chromium carbide
  • 10. Emery
  • 11. Garnet
  • 12. Topaz
  • 13. Siminti
  • 14. Ma'adini
  • 15. Flint
  • 16. Martensite
  • 17. Orthoclase
  • 18. Magnetite
  • 19. Felspar
  • 20. Austenite, Babban CR
  • 21. Pearlite, Alloyed
  • 22. Gilashi
  • 23. Austenite, Low gami
  • 24. Mai tausayawa
  • 25. Pearlite, Unalloyed
  • 26. Austenite, 12% Mn
  • 27. Ferrite
  • 28. Fluorite
  • 29. Karatu
  • 30. Gypsum
  • 31. Carbon
  • 32. Talc
  •  
  • Wodon ƙwararre ne a cikin samar da farantin murfin carbide na Chromium, muna ɗaukar fasahar walƙiyar arc wacce ta ƙunshi ƙarin abun ciki na Cr daga 25% zuwa 45%. ƙaramin ƙarar carbide akan microstructure yana sama da 50% kuma matsakaicin taurin barbashi shine HV1800. Hanyar ASTM-G65 A tana ƙarƙashin 0.16g.
  •  
  • high chromium carbide overlay
  •  
  • Farantin bimetallic na Chromium Carbide:
  •  
  • Matsakaici/Low carbon karfe + Abrasion resistant yadudduka → Chromium carbide bimetallic plate tare da haɗin ƙarfe
  •  
  • (Q235/Q345B + Chromium Carbide mai rufi → Chromium carbide bimetallic plate by Submerged arc or Open arc waldi
  • fasaha)
  • high chromium carbon alloy-
  •  
  •  
  • Detail:
  •  
  • Layer mai jurewa yana da adadi mai yawa na ƙwayoyin carbide mai ƙarfi na chromium. Ana rarraba waɗannan barbashi daidai gwargwado a duk faɗin, yana haifar da ƙananan microstructure. Taurin shine HRC 58~ 65 kuma ya dogara da kaurin rufi.
  •  
  • Babban sinadaran farantin Wodon sune C (%): 3.0 ~6.0 da Cr (%): 25 ~ 45. Wannan gwargwadon sinadaran yana haifar da adadi mai yawa na Cr7C3 chrome carbide hard barbashi. Micro-hardness (har zuwa HV1800) na waɗannan barbashi a duk faɗin Layer zai ba da garantin babban abin da zai iya jurewa.
  •  
  • Rufewa da farantin tushe sune haɗin ƙarfe. Rufewar zai shiga cikin farantin tushe kusan 0.8 ~ 1.8 mm, yana kaiwa har zuwa 350 Mpa a cikin gwajin mu.
  •  
  •  microstructures-chromium carbide overlay wear plate
  • wodon wear clad plate certificate
  •  
  •  
  • WD1200 saka farantin za a iya amfani dashi don aikace -aikacen abrasion mai tsananikuons.
  •  
  • * Rufin carbide na Chromium yana sa farantin mai jurewa
  • * Ta hanyar fasahar walda arc
  • * Haɗin Sinadaran: C: 3.0-6.0% Cr: 25-45%
  • * Chromium carbide Cr7C3 ƙaramin ƙaramin ƙarar kusan 50%
  • * Kauri mai kauri mai kauri zai iya kaiwa 50 mm
  • * Tsarin zafin jiki har zuwa 600 ° C.
  • *Lager daidaitaccen sutturar yanki 1400*3000mm, 1400*3500mm, 2100*3500mm
  • * Better flatness tare da santsi surface
  • * Taurin: HRC58-65 (650-720HV)
  •  
  • Ana amfani da waɗannan faranti sosai a Ma'adinai, Siminti, Wuta, Coal, Port, Wind turbines da Metallurgical masana'antu.
  •  
  •  05chromium carbide overlay wear plate

 

  • 08chromium carbide overlay wear plate

 

  • 09chromium carbide overlay wear plate

 

  • 10chromium carbide overlay wear plate

 

 

 


Lokacin aikawa: Sep-27-2021